Abrasive Material White Fused Alumina pulveris ad molendum Blasting tincidunt
- Color:Pura Alba
- Figura:Cubica et angulata et acuta
- Gravitas specifica:≥ 3.95
- Mohs duritia:9.2 Mohs
- Liquescens punctum:2150℃
- Mole densum;1.50-1.95g/cm3
- Al2O3;99.4%Min
- Na2O:0.30%Max
-
Wfa White Fused Alumina/Aluminium Oxide/Alumina Oxide/Corundum
- AlO3:99.5%
- TiO2;0.0078%
- SiO2 (non gratis);0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda & Potash);0.30%
- Forma crystallis:Rhombohedral Classis
- Natura chemica:Amphotericis
- Gravitas specifica:3.95 grm/cc
- Mole Densitas:116 lbs/ft3
- Duritia:KNOPPS = 2000, MOHS = 9
- Liquescens punctum:2,000°C
-
Corundum 280 Mesh 320 Mesh
- AlO3:99.5%
- TiO2;0.0078%
- SiO2 (non gratis);0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda & Potash);0.30%
- Forma crystallis:Rhombohedral Classis
- Natura chemica:Amphotericis
- Gravitas specifica:3.95 grm/cc
- Mole Densitas:116 lbs/ft3
- Duritia:KNOPPS = 2000, MOHS = 9
- Liquescens punctum:2,000°C
-
JIS Standard White Fused Alumina for Coated Cloth Abrasives White Fused Alumina Wfa
- AlO3:99.5%
- TiO2;0.0078%
- SiO2 (non gratis);0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda & Potash);0.30%
- Forma crystallis:Rhombohedral Classis
- Natura chemica:Amphotericis
- Gravitas specifica:3.95 grm/cc
- Mole Densitas:116 lbs/ft3
- Duritia:KNOPPS = 2000, MOHS = 9
- Liquescens punctum:2,000°C
-
White Corundum JIS/Album Fused Alumina/Wa Abrasive
- AlO3:99.5%
- TiO2;0.0078%
- SiO2 (non gratis);0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda & Potash);0.30%
- Forma crystallis:Rhombohedral Classis
- Natura chemica:Amphotericis
- Gravitas specifica:3.95 grm/cc
- Mole Densitas:116 lbs/ft3
- Duritia:KNOPPS = 2000, MOHS = 9
- Liquescens punctum:2,000°C
-
High Quality Refractory Material White Fused Alumina Grits with Free Sample
- AlO3:99.5%
- TiO2;0.0078%
- SiO2 (non gratis);0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda & Potash);0.30%
- Forma crystallis:Rhombohedral Classis
- Natura chemica:Amphotericis
- Gravitas specifica:3.95 grm/cc
- Mole Densitas:116 lbs/ft3
- Duritia:KNOPPS = 2000, MOHS = 9
- Liquescens punctum:2,000°C